TT - 300

Film grade - TT 300

Description:

Biaxially-oriented transparent polypropylene film for packaging of tobacco goods, with a layer heat sealable on both sides.

Properties:
	Excellent tensile strength at break in both directions
	High water vapour and oxygen barrier properties
	Extended range of heat sealing - from 115°C to 140°C
	Perfect gloss
	Low coefficient of friction
	Physiologic neutrality

Application:
	For wrapping of cigarette packs and blocks

Parameters		Values			Unit	Test method
Thickness		16	20	30	µm	GOST 17035
Weight 1 m²		14,6	18,2	27,3	g	TU U 00203588-24
Yield		68,3	54,9	36,6	m²/kg	TU U 00203588-24
Minimum tensile strength at break	MD	120	130	130	MPa	ASTM D882
Minimum tensile strength at break	TD	230	250	250	MPa	ASTM D882
Maximum elongation at break	MD	220	200	200	%	ASTM D882
Maximum elongation at break	TD	75	65	65	%	ASTM D882
Maximum coefficient of friction, film/film		0,3	0,3	0,45	-	ASTM D1894
Minimum seal strength		2,0	2,5	3,0	N/15mm	125°C; 1,5 bar; 1s.
Maximum thermal shrinkage	MD	4	4	4	%	ASTM D1204 (120°C, 15min)
Maximum thermal shrinkage	TD	2	2	2	%	ASTM D1204 (120°C, 15min)
Film haze (max)		2,2	2,3	2,5	%	ASTM D1003
Gloss (min)		85	85	85	%	ASTM D2457
Surface treatment		-	-	38-40	dyne/cm	ASTM D2578

ATTENTION! Information presented should be considered as reference and could not be used as commercial. In any case, before making a decision about commercial deliveries, it is recommended to conduct tests intended to confirm compliance of our products to the actual conditions of application.