| Film
grade - LT 300, LT 310 |
| Description: |
| Biaxially-oriented
transparent label polypropylene film (LT300), label for PET-bottles
on the basis of biaxially-oriented transparent polypropylene film
with print (LT310). |
|
| Properties: |
 |
Excellent
tensile strength at break in both directions |
|
Perfect
gloss |
|
Stable
coefficient of friction |
|
Physiologic
neutrality |
|
| Application: |
|
For production
of labels for PET-bottles |
|
For labeling
of PET-bottles mainly in production of transparent goods, for example,
mineral and table water |
|
|
|
Parameters
|
Values |
Unit |
Test
method
|
|
Thickness
|
40 |
µm |
GOST
17035
|
|
Weight
1 m2
|
36,5 |
g |
TU
U 00203588-24
|
|
Yield
|
27,4 |
m2/kg |
TU
U 00203588-24
|
|
Minimum
tensile strength at break
|
MD |
130 |
MPa |
ASTM
D882
|
| TD |
250 |
|
Maximum
elongation at break
|
MD |
200 |
% |
ASTM
D882
|
| TD |
65 |
|
Maximum
coefficient of friction, film/film
|
0,45 |
- |
ASTM
D1894
|
|
Minimum
seal strength
|
3,5 |
N/15mm |
125°C;
1,5 bar; 1s.
|
|
Maximum
thermal shrinkage
|
MD |
4 |
% |
ASTM
D1204
(120°C, 15min)
|
| TD |
2 |
|
Film
haze (max)
|
2,7 |
% |
ASTM
D1003
|
|
Gloss
(min)
|
85 |
% |
ASTM
D2457
|
|
Surface
treatment
|
38-40 |
dyne/cm |
ASTM
D2578
|
|
| |
|
ATTENTION! Information presented
should be considered as reference and could not be used as commercial.
In any case, before making a decision about commercial deliveries, it
is recommended to conduct tests intended to confirm compliance of our
products to the actual conditions of application.
|