| Film
grade - LP 200, LP 211 |
| Description: |
| Biaxially-oriented
opaque white-pearlescent label polypropylene film (LP 200), label
for PET-bottles on the basis of biaxially-oriented opaque white-pearlescent
polypropylene film with print (LP 211). |
|
|
|
| Properties: |
 |
Physiologic
neutrality |
|
Low specific
density |
|
Opacity |
|
High resistance
to tear and puncture |
|
High gloss |
|
Low coefficient
of friction |
|
High resistance
of printing to mechanical damage |
|
| Application: |
|
For manufacture
of labels for PET- bottles |
|
For printing |
|
For labeling
of PET-bottles. It is recommended for manufacture of opaque or coloured
drinks: beer, kvass, fruit drinks, etc. |
|
|
|
Parameters
|
Values |
Unit |
Test
method |
|
Thickness
|
40 |
µm |
GOST
17035 |
|
Weight
1 m2
|
26,0 |
g |
TU
U 00203588-24 |
|
Yield
|
38,5 |
m2/kg |
TU
U 00203588-24 |
|
Minimum
tensile strength at break
|
MD |
65 |
MPa |
ASTM D882 |
|
TD |
110 |
|
Maximum
elongation at break
|
MD |
140 |
% |
ASTM D882 |
|
TD |
40 |
|
Maximum
coefficient of friction, film/film
|
0,45 |
- |
ASTM D 1894 |
|
Minimum
seal strength
|
2,3 |
N/15mm |
125°C; 1,5 bar; 1s. |
|
Maximum
thermal shrinkage
|
MD |
4,0 |
% |
ASTM D1204
(120°C, 15min) |
| TD |
2,0 |
| Maximum
transparency |
30 |
% |
ASTM
D 1003 |
| Surface
treatment |
38-41 |
dyne/cm |
ASTM
D 2578 |
|
| |
ATTENTION!
Information presented should be considered as reference and could
not be used as commercial. In any case, before making a decision about
commercial deliveries, it is recommended to conduct tests intended
to confirm compliance of our products to the actual conditions of
application.
|