Film grade - GT 100
Description:
Biaxially-oriented transparent polypropylene film for general application without heat sealable layers (mono).
Properties:
Excellent tensile strength at break in both directions
Superior rigidity
Good transparency and gloss
Physiologic neutrality
Application:
For lamination
For souvenir wrapping of flowers

Parameters

 Values Unit Test method
Thickness
 30 35 µm GOST 17035
Weight 1 m2
 27,3 31,85 g TU U 00203588-24
Yield
 36,6 31,4 m2/kg TU U 00203588-24
Minimum tensile strength at break
 MD 130 130 MPa ASTM D882
TD 250 250
Maximum elongation at break
 MD 200 200 % ASTM D882
TD 65 65
Maximum coefficient of friction, film/film
 0,7 0,7 - ASTM D1894
Minimum seal strength
 - N/15mm 125°C; 1,5 bar; 1s.
Maximum thermal shrinkage
 MD 4,0 4,0 % ASTM D1204
(120°C, 15min)
TD 2,0 2,0
Film haze (max) 1,8 1,9 % ASTM D1003
Gloss (min) 85 85 % ASTM D2457
Surface treatment
 38-40 38-40 dyne/cm ASTM D2578
 
ATTENTION! Information presented should be considered as reference and could not be used as commercial. In any case, before making a decision about commercial deliveries, it is recommended to conduct tests intended to confirm compliance of our products to the actual conditions of application.