GM - 201

Film grade - GM 201

Description:
Biaxially-oriented polypropylene film for general application, metallized and coated with primer on one side and having a heat sealable layer on the other side.

Properties:
	Excellent tensile strength at break in both directions
	Physiologic neutrality
	High water vapour and oxygen barrier properties
	High adhesion of aluminium to film
	Good gloss
	Extended range of heat sealing - from 115°C to 140°C
	High seal strength
	Exsellent adhesion of printing ink to metallized surface

Application:
	For printing

Parameters		Values			Unit	Test method
Thickness		20	30	35	µm	GOST 17035
Weight 1 m²		18,7	27,8	32,3	g	TU U 00203588-24
Yield		53,5	36,0	31,0	m²/kg	TU U 00203588-24
Minimum tensile strength at break	MD	130	130	130	MPa	ASTM D882
Minimum tensile strength at break	TD	250	250	250	MPa	ASTM D882
Maximum elongation at break	MD	200	200	200	%	ASTM D882
Maximum elongation at break	TD	65	65	65	%	ASTM D882
Maximum coefficient of friction, film/film		0,7	0,7	0,7	-	ASTM D1894
Minimum seal strength		2,5	3,0	3,0	N/15mm	125°C; 1,5 bar; 1s.
Maximum thermal shrinkage	MD	4,0	4,0	4,0	%	ASTM D1204 (120°C, 15min)
Maximum thermal shrinkage	TD	2,0	2,0	2,0	%	ASTM D1204 (120°C, 15min)
Optical density		1,8-2,3	1,8-2,3	1,8-2,3	-	-

ATTENTION! Information presented should be considered as reference and could not be used as commercial. In any case, before making a decision about commercial deliveries, it is recommended to conduct tests intended to confirm compliance of our products to the actual conditions of application.