BIPAN
Film grade - GM 200, GM 210
Description:
Biaxially-oriented polypropylene film for general application, metallized on one side and having a heat sealable layer on the other side (GM 200), biaxially-oriented polypropylene film for general application, metallized on one side and having a heat sealable layer on the other side, with print (GM 210).
Properties:
Excellent tensile strength at break in both directions
Physiologic neutrality
High water vapour and oxygen barrier properties
High adhesion of aluminium to film
Good gloss
Extended range of heat sealing - from 115°C to 140 °C
High seal strength
Application:
For printing
For lamination
For packaging of various foodstuffs and manufactured goods

Parameters

 Values Unit Test method
Thickness
 20 30 35 µm GOST 17035
Weight 1 m2
 18,2 27,3 31,85 g TU U 00203588-24
Yield
 54,9 36,6 31,4 m2/kg TU U 00203588-24
Minimum tensile strength at break
 MD 130 130 130 MPa ASTM D882
TD 250 250 250
Maximum elongation at break
 MD 200 200 200 % ASTM D882
TD 65 65 65
Maximum coefficient of friction, film/film
 0,7 0,7 0,7 - ASTM D1894
Minimum seal strength
 2,5 3,0 3,0 N/15mm 125°C; 1,5 bar; 1s.
Maximum thermal shrinkage
 MD 4,0 4,0 4,0 % ASTM D1204
(120°C, 15min)
TD 2,0 2,0 2,0
Optical density
 1,8-2,3 1,8-2,3 1,8-2,3 - -
 
ATTENTION! Information presented should be considered as reference and could not be used as commercial. In any case, before making a decision about commercial deliveries, it is recommended to conduct tests intended to confirm compliance of our products to the actual conditions of application.