GM - 100

Film grade - GM 100

Description:
Metallized biaxially-oriented polypropylene film for general application without heat sealable layers (mono).

Properties:
	Excellent tensile strength at break in both directions
	Physiologic neutrality
	High water vapour and oxygen barrier properties
	High adhesion of aluminium to film
	Good gloss

Application:
	For printing
	For lamination
	For souvenir wrapping of flowers

Parameters		Values		Unit	Test method
Thickness		30	35	µm	GOST 17035
Weight 1 m²		27,3	31,85	g	TU U 00203588-24
Yield		36,6	31,4	m²/kg	TU U 00203588-24
Minimum tensile strength at break	MD	130	130	MPa	ASTM D882
	TD	250	250
Maximum elongation at break	MD	200	200	%	ASTM D882
	TD	65	65
Maximum coefficient of friction, film/film		0,7	0,7	-	ASTM D1894
Minimum seal strength		-		N/15mm	125°C; 1,5 bar; 1s.
Maximum thermal shrinkage	MD	4,0	4,0	%	ASTM D1204 (120°C, 15min)
	TD	2,0	2,0
Optical density		1,8-2,3	1,8-2,3	-	-

ATTENTION! Information presented should be considered as reference and could not be used as commercial. In any case, before making a decision about commercial deliveries, it is recommended to conduct tests intended to confirm compliance of our products to the actual conditions of application.